Polymer Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/ Hasa International trade goods import and export Thu, 06 Nov 2025 12:15:16 +0000 en-US hourly 1 https://wordpress.org/?v=6.9 https://hasacom.com/en/wp-content/uploads/2023/01/cropped-favicon-1-32x32.png Polymer Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/ 32 32 XLPE Compound for Low / Medium Voltage Cable Insulation https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/ https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/#respond Sun, 02 Nov 2025 11:27:12 +0000 https://hasacom.com/en/?post_type=product&p=1906 XBC-955 is a high-performance cross-linkable polyethylene (XLPE) compound engineered for low ...

XLPE Compound for Low / Medium Voltage Cable Insulation yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> XBC-955 is designed for the insulation of low & medium voltage (LV/MV) cables, offering superior thermal stability, dielectric strength, and mechanical integrity after curing.
It is suitable for moisture-cure, silane, or catalyst-based cross-linking systems and provides a smooth extrusion surface and consistent output on standard PE extrusion lines.

Applications:

  • Low and Medium Voltage Cable Insulation

  • Electrical Power Cables and Conductors

  • Building and Industrial Wire Insulation

Form: Natural Pellets
Process: Extrusion (Moisture / Silane Cross-Linking)

Key Features

  • Excellent mechanical properties after cross-linking

  • High tensile strength and elongation

  • Superior electrical insulation and volume resistivity

  • Good surface finish and extrusion stability

  • Compatible with moisture and silane cross-linking systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 0.935 ± 0.005
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1.5 ± 0.5
Tensile Strength ISO 527 MPa 22
Elongation at Break ISO 527 % 700
Hardness ISO 868 Shore D 58
Melting Point ISO 11357 °C 127
Oxidation Induction Time (200 °C) ISO 11357 min 60
ESCR (50 °C, F50) ISO 22088 h > 1000
Gel Content (After Cross-Linking) ISO 10147 % ≥ 65

Processing Recommendations

  • Barrel Temperature: 150 – 230 °C

  • Die Head Temperature: 230 – 240 °C

  • Suitable for PE screw extruders

  • Ensure moisture-free feeding and proper degassing for optimal cross-linking

Packaging & Storage

Supplied in 25 kg sacks.
Store in a cool, dry, clean area, away from sunlight and heat.
Recommended storage period: max 2 years.

XLPE Compound for Low / Medium Voltage Cable Insulation yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/feed/ 0 White Masterbatch with TiO₂ https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/ https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/#respond Sun, 02 Nov 2025 10:59:17 +0000 https://hasacom.com/en/?post_type=product&p=1901 WTP-270 is a white polyethylene-based masterbatch containing 20–70% high-quality ...

White Masterbatch with TiO₂ yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> WTP-270 is a PE-based white masterbatch designed to enhance brightness, color consistency, and surface finish in extrusion, injection, and blow molding processes.
The compound ensures excellent optical performance and processability, suitable for both monolayer and multilayer production lines.

Applications
General-purpose plastic goods
Packaging films and shopping bags
Containers, bottles, and household items
Automotive and industrial parts

Form: White Pellets
Process: Extrusion, Injection, Blow Molding

Key Features
High opacity and whiteness with TiO₂ content up to 70%
Excellent UV and heat stability
Smooth surface and uniform color dispersion
High coverage and processability
Suitable for LDPE, LLDPE, and HDPE systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 1.0 – 1.7
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1 – 3
Filler Content (TiO₂) ISO 3451 % 20 – 70
Tensile Strength ISO 527 MPa 16 – 20
Elongation at Break ISO 527 % 300 – 500
Hardness ISO 868 Shore D 55 – 60
Vicat Softening Temperature ISO 306 °C 128
Oxidation Induction Time ISO 11357 min 30
Moisture Content ISO 15512 % < 0.25

Processing Guidelines
Barrel Temperature: 150–220 °C
Die Head Temperature: 220–230 °C
Suitable for standard PE screw extruders
Recommended for high-speed film, sheet, and molding lines

Packaging & Storage
Supplied in 25 kg sacks or 850 kg big bags.
Store in original packaging under cool, dry conditions, protected from sunlight and heat.
Shelf life: 2 years from manufacturing date.

White Masterbatch with TiO₂ yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/feed/ 0 PE-Based Black Masterbatch https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/ https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/#respond Sun, 02 Nov 2025 10:41:05 +0000 https://hasacom.com/en/?post_type=product&p=1898 BCP-460 is a black polyethylene-based masterbatch containing 40% ultrafine ...

PE-Based Black Masterbatch yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> BCP-460 is engineered for general-purpose plastic applications, delivering high color uniformity, durability, and excellent dispersion.
Its formulation with antioxidants (AO), process aid (PPA), and functional fillers ensures consistent performance in both monolayer and multilayer extrusion systems.

Applications:

  • Pipes and conduit systems

  • Cable sheathing and insulation

  • Films and sheets

  • Household and automotive parts

Form: Black pellets
Process: Extrusion, Injection, Blow Molding

Key Features

  • 40% ultrafine carbon black content

  • Deep black tone and high opacity

  • Excellent dispersion and surface smoothness

  • UV and thermal stability

  • Wide processing temperature range

  • Suitable for LDPE, LLDPE, and HDPE systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 1.2 ± 0.1
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1 ± 0.5
Filler Content (Carbon Black) ISO 3451 % 40
Tensile Strength ISO 527 MPa 22
Elongation at Break ISO 527 % 700
Hardness ISO 868 Shore D 60
Vicat Softening Point ISO 306 °C 129
Oxidation Induction Time ISO 11357 min 30
Moisture Content ISO 15512 % < 0.25

Processing Guidelines

  • Barrel Temperature: 150–220 °C

  • Die Head Temperature: 220–230 °C

  • Compatible with standard PE screws

  • Excellent output and dispersion across multiple processing types

Packaging & Storage

Supplied in 25 kg bags or 850 kg big bags.
Store in original packaging under cool, dry conditions, away from sunlight and heat.
Recommended shelf life: 2 years.

PE-Based Black Masterbatch yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/feed/ 0 CaCO₃ Calcium Carbonate Filled PE Compound https://hasacom.com/en/urun/caco%e2%82%83-calcium-carbonate-filled-polyethylene-compound/ https://hasacom.com/en/urun/caco%e2%82%83-calcium-carbonate-filled-polyethylene-compound/#respond Sun, 02 Nov 2025 10:26:51 +0000 https://hasacom.com/en/?post_type=product&p=1894 CFP-180 is a cost-optimized, calcium carbonate filled polyethylene compound containing 10–80% ...

CaCO₃ Calcium Carbonate Filled PE Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> CFP-180 is a CaCO₃-filled polyethylene masterbatch engineered to improve mechanical and surface performance of polyolefin products.
It provides higher rigidity, gloss, and print adhesion, making it ideal for film, sheet, molding, and cable applications.

Applications:

  • Packaging films and sheets

  • Containers and bottles

  • Household and industrial goods

  • Cable sheathing and insulation

Form: Natural / White Pellets
Processing: Extrusion, Injection, Blow Molding

Key Features

  • Cost-effective filler compound for PE systems

  • Enhanced stiffness and surface finish

  • Excellent printability and dimensional stability

  • Wide processing window

  • Compatible with LDPE, LLDPE, and HDPE

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 0.96–1.60
Melt Flow Rate (190 °C / 5 kg) ISO 1133 g/10 min 0.5–2
Filler Content ISO 3451 % 10–80
Tensile Strength ISO 527 MPa 15–20
Elongation at Break ISO 527 % 300–500
Hardness ISO 868 Shore D 55–65
Vicat Softening Point ISO 306 °C 126
Oxidation Induction Time ISO 11357 min 20
Moisture Content ISO 15512 % < 0.25

Processing Guidelines

  • Extruder Barrel Temp: 150–220 °C

  • Die Head Temp: 220–230 °C

  • Suitable for most PE extrusion and molding lines

  • Recommended for PE screws and high-output systems

Packaging & Storage

Supplied in 25 kg bags or 850 kg big bags.
Store in original packaging, in a cool, dry, and clean area, away from sunlight and heat.
Shelf life: up to 2 years.

CaCO₃ Calcium Carbonate Filled PE Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/caco%e2%82%83-calcium-carbonate-filled-polyethylene-compound/feed/ 0 HDPE UV-Stabilized Jacketing Compound https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/ https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/#respond Sun, 02 Nov 2025 10:00:49 +0000 https://hasacom.com/en/?post_type=product&p=1891 JAC03-UV is a UV-stabilized high-density polyethylene (HDPE) compound designed for cable ...

HDPE UV-Stabilized Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC03-UV is a natural-colorable HDPE compound with UV stabilizers and antioxidants for enhanced long-term durability.
It offers superior resistance to UV radiation, oil and termite attack, and excellent surface quality during extrusion.
The compound meets ASTM D1248 Type III Class A Category 5 Grade J5, IEC 60502 ST7, IEC 60840 ST7, and IEC 60708 standards.

Key Features

  • Excellent UV resistance and outdoor stability

  • Termite and oil resistance (UL 1072 Type I & II)

  • Low water permeability

  • Excellent environmental stress crack resistance (ESCR > 5000 h)

  • High tensile strength and elongation

  • Smooth surface extrusion and easy processing

Technical Specifications

Property Typical Value Test Method
Density 0.943 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) 0.33 ± 0.05 g/10 min ASTM D1238
Tensile Strength ≥ 27 N/mm² ASTM D638 / IEC 60811-1-1
Elongation at Break ≥ 800 % ASTM D638
Elongation after Ageing (10 days @ 110 °C) ≥ 500 % ASTM D638
Oxidation Induction Time (200 °C) ≥ 30 min ASTM D3895
ESCR (50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 60 ± 2 Shore D ASTM D2240
Vicat Softening Point ≥ 115 °C ISO 306
Hot Pressure Test (110 °C) < 50 % IEC 60811-3-1
Water Absorption ≤ 0.01 % ASTM D570
Volume Resistivity ≥ 10¹⁵ Ω·cm IEC 60093
Dielectric Strength (2 mm) No breakdown @ 10 kV/mm IEC 60243

Processing Recommendations

Recommended extrusion temperature profile (°C):
Zone 1 – 160–180 | Zone 2 – 170–190 | Zone 3 – 180–200 | Zone 4 – 190–210 | Head – 210–230 | Die – 240–260

Provides a smooth extrusion surface; adjust profile according to extruder type.

Applications

  • Outer jacketing for power and telecommunication cables

  • Outdoor UV-resistant cable systems

  • Industrial, marine, and energy cables exposed to sunlight

Packaging & Safety

Supplied in 25 kg PP laminated bags (pellet form).
Store below 30 °C, away from sunlight and humidity.
Classified as non-hazardous material.

HDPE UV-Stabilized Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/feed/ 0 Black LLDPE Jacketing Compound https://hasacom.com/en/urun/black-lldpe-jacketing-compound/ https://hasacom.com/en/urun/black-lldpe-jacketing-compound/#respond Sun, 02 Nov 2025 08:14:04 +0000 https://hasacom.com/en/?post_type=product&p=1888 JAC04 is a black linear low-density polyethylene (LLDPE) compound designed for ...

Black LLDPE Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC04 is a carbon black-filled (2.5%) LLDPE compound optimized for cable jacketing applications.
Its high melting temperature, excellent petroleum-jelly resistance, and low moisture permeability ensure long-term cable durability under demanding environments.
The compound provides a smooth extrusion surface, broad processing window, and superior mechanical flexibility.

Complies with: ASTM D1248 Type 2, Class C, Category 4, Grade J3,

E5 IEC 60502 ST7 | EN 50290-2-23

Key Features

  • Excellent weathering and UV resistance (2.5% carbon black)

  • Good petroleum-jelly and oil resistance

  • Low water permeability

  • Superior ESCR (Environmental Stress Crack Resistance > 5000 h)

  • High tensile and elongation properties

  • Wide extrusion temperature range (140–230 °C)

  • Non-hazardous material

Technical Specifications

Property Typical Value Test Method
Density 0.935 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) ≤ 1.0 g/10 min ASTM D1238
Tensile Strength ≥ 20 N/mm² ASTM D638
Elongation at Break ≥ 800 % ASTM D638
Elongation after Ageing (240 h / 110 °C) ≥ 300 % ASTM D638
ESCR (Condition A, 50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 56 ± 2 Shore D ASTM D2240
Brittleness Temperature < –70 °C ASTM D746
O.I.T. (200 °C) > 100 min ASTM D3895
Carbon Black Content 2.5 % ASTM D1603
Carbon Black Dispersion ≤ 2 ISO 18553
Volume Resistivity 10¹⁵ Ω·cm IEC 60093
Dielectric Strength (2 mm) ≥ 20 kV/mm IEC 60243
Dielectric Constant (1 MHz) ≤ 2.3 ASTM D150
Dissipation Factor (1 MHz) ≤ 0.005 ASTM D150

Processing Recommendations

Recommended extrusion temperature profile (°C): Zone 1 – 140–160 | Zone 2 – 150–170 | Zone 3 – 160–180 | Zone 4 – 170–190 | Head – 200–220 | Die – 210–230
Preheating/drying max 80 °C.

Applications

  • Outer jacketing for power and communication cables

  • Outdoor and underground cable systems requiring UV and jelly resistance

  • Industrial and telecommunication installations

Packaging & Storage

Supplied as pellets in 25 kg PP laminated bags.
Store below 30 °C, away from direct sunlight and moisture.
Classified as non-hazardous.

Black LLDPE Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/black-lldpe-jacketing-compound/feed/ 0 Black HDPE Compound for Cable Jacketing https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/ https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/#respond Sun, 02 Nov 2025 08:02:54 +0000 https://hasacom.com/en/?post_type=product&p=1885 JAC05 is a black high-density polyethylene (HDPE) compound designed ...

Black HDPE Compound for Cable Jacketing yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC05 is a specially formulated HDPE compound used for the sheathing and insulation of power and communication cables.
The compound ensures outstanding weathering resistance, UV stability, termite protection, and mechanical strength under outdoor exposure.
Complies with ASTM D1248 Type III, Class C, Cat.5, Grade J5, IEC 60502 ST7, IEC 60840 ST7, IEC 60708 standards.

Key Features

  • Excellent UV resistance (2.5% carbon black)

  • Termite and oil resistance (UL 1072 Type I & II)

  • Superior ESCR (Environmental Stress Crack Resistance > 5000 h)

  • Low water permeability and weather stability

  • High mechanical strength and flexibility

  • Excellent surface finish during extrusion

Technical Specifications

Property Typical Value Test Method
Density 0.945 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) 0.29 ± 0.03 g/10 min ASTM D1238
Carbon Black Content 2.5 % ASTM D1603
Tensile Strength ≥ 25 N/mm² ASTM D638 / IEC 60811-1-1
Elongation at Break ≥ 700 % ASTM D638 / IEC 60811-1-1
Elongation after Ageing (14 days / 110 °C) ≥ 500 % ASTM D638
O.I.T. (Oxidation Induction Time @ 200 °C) ≥ 30 min ASTM D3895
ESCR (Condition B, 50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 57 ± 1 Shore D ASTM D2240
Oil Immersion (70 °C, 4 h) Δ Tensile / Δ Elong. < 20 % / < 40 % ASTM D2633
Carbon Black Dispersion ≤ 2.5 ISO 18553
Hot Pressure Test (110 °C) < 50 % IEC 60811-3-1
Volume Resistivity ≥ 10¹⁶ Ω·cm IEC 60093
Dielectric Strength (2 mm) No breakdown @ 10 kV/mm IEC 60243

Processing Guidelines

Recommended Extrusion Temperatures (°C):

Zone 1 – 140–160 | Zone 2 – 150–170 | Zone 3 – 160–180 | Zone 4 – 170–190 | Head – 200–210 | Die – 210–220

Provides excellent surface quality; adjust temperatures according to extruder design.

Applications

  • Outer jacketing and insulation of power & communication cables

  • Outdoor cable systems requiring UV & oil resistance

  • Underground and termite-prone environments

Packaging & Safety

Supplied in 25 kg PP laminated bags (pellet form).
Store below 30 °C, away from sunlight and moisture.
Classified as non-hazardous material.

Black HDPE Compound for Cable Jacketing yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/feed/ 0 HFFR Halogen-Free Flame-Retardant Jacketing Compound https://hasacom.com/en/urun/hffr-halogen-free-uv-oil-resistant-flame-retardant-jacketing-compound-lsj01-or/ https://hasacom.com/en/urun/hffr-halogen-free-uv-oil-resistant-flame-retardant-jacketing-compound-lsj01-or/#respond Sat, 01 Nov 2025 17:33:18 +0000 https://hasacom.com/en/?post_type=product&p=1876 LSJ01-OR is a halogen-free, UV- and oil-resistant, low-smoke, flame-retardant thermoplastic compound ...

HFFR Halogen-Free Flame-Retardant Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> LSJ01-OR is a thermoplastic halogen-free compound formulated for power and control cable sheathing where weather, UV, and oil resistance are required.
It exhibits superior fire performance, smooth extrusion, and long-term durability under outdoor exposure.
The compound meets IEC 60502-1 (ST8), IEC 60092-359 (SHF1), BS 7655, VDE 0250 HM2/HM4, and EN 50575 requirements.

Key Features

  • Halogen-free, low smoke, flame-retardant

  • UV-resistant and oil-resistant for outdoor use

  • High tensile strength and flexibility

  • Excellent extrusion surface finish

  • Stable mechanical and electrical properties

  • Safe, non-hazardous compound

Technical Specifications

Property Typical Value Test Method
Density 1.45 ± 0.02 g/cm³ IEC 60811-1-3
Tensile Strength ≥ 13 N/mm² IEC 60811-1-1
Elongation at Break ≥ 200 % IEC 60811-1-1
Ageing (7 days @ 100 °C) ΔTensile / ΔElong. ± 40 % / ± 40 % IEC 60811-1-2
Tear Strength 10 N/mm BS 6469:99.1
Hardness 52 ± 2 Shore D ASTM D2240
Melt Flow Index (150 °C / 21.6 kg) 3 g/10 min ASTM D1238
Heat Shock (150 °C / 1 h) No Cracks IEC 60811-3-1
Oil Immersion (70 °C / 4 h) ΔTensile / ΔElong. ≤ 20 % / ≤ 40 % —
UV Exposure (720 h) Retention Tensile / Elong. 86 % / 86 % ASTM G154
Oxygen Index ≥ 32 % ASTM D2863
pH / Conductivity > 5 / ≤ 10 µS/mm IEC 60754-2
Halogen Acid Gas Evolution 0 % IEC 60754-1
Smoke Density 8 % ASTM D2843
Light Transmission 70 % IEC 61034
Toxicity Index 1.7 NES 713
Cold Bend / Impact Pass IEC 60811-1-4

Processing Recommendations

  • Extruder Compression Ratio: 1 : 1.2 (low shear screw recommended)

  • Typical Temperature Profile (°C):
    Zone 1 – 130–140 | Zone 2 – 140–145 | Zone 3 – 145–150 | Zone 4 – 150–155 | Head – 160–165 | Die – 165–175

  • Compatible with PE/EVA-based masterbatches

  • Classified as non-hazardous material

Applications

  • Outer sheathing of power and control cables

  • Outdoor LSZH cables requiring UV & oil resistance

  • Industrial, marine, and energy cable systems

Packaging & Storage

Supplied in 25 kg PP laminated bags (pellet form).
Store below 30 °C, away from sunlight and humidity.
Do not stack directly on the ground.

HFFR Halogen-Free Flame-Retardant Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/hffr-halogen-free-uv-oil-resistant-flame-retardant-jacketing-compound-lsj01-or/feed/ 0 HFFR Halogen-Free Flame-Retardant Bedding Compound https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-bedding-compound-lsb01/ https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-bedding-compound-lsb01/#respond Sat, 01 Nov 2025 16:43:18 +0000 https://hasacom.com/en/?post_type=product&p=1870 LSB01 is a halogen-free, flame-retardant thermoplastic compound developed for cable bedding ...

HFFR Halogen-Free Flame-Retardant Bedding Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> LSB01 is a polyolefin-based thermoplastic compound containing a specialized flame-retardant system that provides self-extinguishing properties without the release of halogen acids.
It significantly reduces smoke, toxicity, and corrosive gas emissions, making it suitable for use in public buildings, transportation, tunnels, and high-safety cable installations.

Complies with: IEC 60502 Type ST8

Color: Natural

Key Features

  • Halogen-free and low smoke emission

  • Excellent self-extinguishing fire performance

  • Stable extrusion and smooth surface finish

  • Good flexibility and impact resistance

  • Low water absorption and no cracks after heat or cold testing

  • Safe, non-hazardous compound

Technical Specifications

Property Typical Value Test Method
Density 1.49 ± 0.03 g/cm³ ASTM D792 / IEC 60811-1-3
Tensile Strength ≥ 9 N/mm² IEC 60811-1-1
Elongation at Break ≥ 125 % IEC 60811-1-1
Ageing Variation (7 days at 100 °C) ±40 % IEC 60811-1-2
Hardness 55 ± 1 Shore D ASTM D2240
Melt Flow Index (150 °C / 21.6 kg) 2 ± 0.5 g/10 min ASTM D1238
Heat Shock (1 h at 150 °C) No Cracks IEC 60811-3-1
Water Absorption ≤ 10 mg/cm² IEC 60811-1-3
Cold Bending Pass IEC 60811-1-4
Cold Impact Pass IEC 60811-1-4
Oxygen Index ≥ 30 % ASTM D2863
pH / Conductivity > 4.3 / ≤ 10 µS/mm IEC 60754-2
Flame Spread > 50 mm IEC 60332-1

Processing Recommendations

Typical extrusion temperature zones (°C):
Zone 1 – 130–150 | Zone 2 – 130–160 | Zone 3 – 140–160 | Zone 4 – 140–160 | Head – 150–170 | Die – 150–170
Drawdown ratio: 1.2–1.8  L/D ratio ≈ 22
Use low-shear screws and controlled line speeds for best surface quality.

Applications

  • Bedding and filler layer in LSZH cables

  • Power and control cables requiring halogen-free fire protection

  • Building, industrial, marine, and public infrastructure cabling

Packaging & Storage

Supplied in 25 kg PP laminated bags in pellet form.
Store below 30 °C, away from direct sunlight and moisture.
Keep bags sealed until use.

HFFR Halogen-Free Flame-Retardant Bedding Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-bedding-compound-lsb01/feed/ 0 HFFR Halogen-Free Thermoplastic Jacketing Compound https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-jacketing-compound-lsj01/ https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-jacketing-compound-lsj01/#respond Sat, 01 Nov 2025 16:13:38 +0000 https://hasacom.com/en/?post_type=product&p=1866 LSJ01 is a halogen-free, low-smoke, flame-retardant thermoplastic compound designed for cable ...

HFFR Halogen-Free Thermoplastic Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> LSJ01 is a halogen-free, flame-retardant compound formulated for the outer sheathing of power and control cables.
It offers excellent processability, mechanical strength, UV resistance, and fire safety.
The compound is suitable for both indoor and outdoor LSZH (Low Smoke Zero Halogen) cable systems and complies with key international standards.

Applicable Standards: IEC 60502-1 Type ST8 | IEC 60092-359 Type SHF1 | BS 7655:6.1 | DIN VDE 0207 / 0250 HM2-HM4 | BS EN 50575

Key Features

  • Halogen-Free and Low Smoke (LSZH)

  • Excellent Flame Retardancy (Oxygen Index ≥ 32 %)

  • UV Resistance for Outdoor Cables

  • High Flexibility and Mechanical Strength

  • No Cracks under Heat or Cold Conditions

  • Excellent Surface Finish and Easy Extrusion

Technical Specifications

Property Typical Value Test Method
Density 1.45 ± 0.02 g/cm³ IEC 60811-601
Tensile Strength ≥ 12 N/mm² IEC 60811-1-1
Elongation at Break ≥ 175 % IEC 60811-1-1
Ageing (7 days at 100 °C) – Δ Tensile / Δ Elongation ±30 % / ±30 % IEC 60811-1-2
Tear Strength 8 N/mm BS 6469:99.1
Hardness 55 ± 1 Shore D ASTM D2240
MFI (150 °C / 21.6 kg) 7 ± 1 g/10 min ASTM D1238
Heat Shock (1 h at 150 °C) No Cracks IEC 60811-3-1
UV Exposure (720 h) Retained Tensile / Elongation 86 % / 86 % ASTM G154
Hot Pressure (90 °C) ≤ 30 % IEC 60811-3-1
Cold Bend / Impact Pass IEC 60811-1-4
Oxygen Index ≥ 32 % ASTM D2863
pH / Conductivity > 4.3 / ≤ 10 µS/mm IEC 60754-2
Halogen Acid Gas 0 % IEC 60754-1
Smoke Density 8 % ASTM D2843
Toxicity Index 1.7 NES 713
Flame Spread > 5 mm IEC 60332-1

Processing Recommendations

  • Use low-compression (1:1.2), low-shear screws for optimal extrusion.

  • Typical temperature profile (°C):
    Zone 1 – 130-140 | Zone 2 – 140-145 | Zone 3 – 145-150 | Head – 155-165 | Die – 165-175

  • Suitable for PE/EVA masterbatch colorants.

  • Classified as non-hazardous material.

Applications

  • Outer sheathing of power and control cables

  • Indoor and outdoor LSZH cable jackets

  • UV-resistant cable systems for industrial, marine, and building sectors

Packaging & Storage

Supplied in 25 kg PP laminated bags.
Store below 30 °C, away from sunlight and humidity.
Do not stack directly on the ground.

HFFR Halogen-Free Thermoplastic Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/hffr-halogen-free-flame-retardant-thermoplastic-jacketing-compound-lsj01/feed/ 0