Masterbatches Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/masterbatches/ Hasa International trade goods import and export Wed, 05 Nov 2025 11:36:18 +0000 en-US hourly 1 https://wordpress.org/?v=6.9 https://hasacom.com/en/wp-content/uploads/2023/01/cropped-favicon-1-32x32.png Masterbatches Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/masterbatches/ 32 32 White Masterbatch with TiO₂ https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/ https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/#respond Sun, 02 Nov 2025 10:59:17 +0000 https://hasacom.com/en/?post_type=product&p=1901 WTP-270 is a white polyethylene-based masterbatch containing 20–70% high-quality ...

White Masterbatch with TiO₂ yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> WTP-270 is a PE-based white masterbatch designed to enhance brightness, color consistency, and surface finish in extrusion, injection, and blow molding processes.
The compound ensures excellent optical performance and processability, suitable for both monolayer and multilayer production lines.

Applications
General-purpose plastic goods
Packaging films and shopping bags
Containers, bottles, and household items
Automotive and industrial parts

Form: White Pellets
Process: Extrusion, Injection, Blow Molding

Key Features
High opacity and whiteness with TiO₂ content up to 70%
Excellent UV and heat stability
Smooth surface and uniform color dispersion
High coverage and processability
Suitable for LDPE, LLDPE, and HDPE systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 1.0 – 1.7
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1 – 3
Filler Content (TiO₂) ISO 3451 % 20 – 70
Tensile Strength ISO 527 MPa 16 – 20
Elongation at Break ISO 527 % 300 – 500
Hardness ISO 868 Shore D 55 – 60
Vicat Softening Temperature ISO 306 °C 128
Oxidation Induction Time ISO 11357 min 30
Moisture Content ISO 15512 % < 0.25

Processing Guidelines
Barrel Temperature: 150–220 °C
Die Head Temperature: 220–230 °C
Suitable for standard PE screw extruders
Recommended for high-speed film, sheet, and molding lines

Packaging & Storage
Supplied in 25 kg sacks or 850 kg big bags.
Store in original packaging under cool, dry conditions, protected from sunlight and heat.
Shelf life: 2 years from manufacturing date.

White Masterbatch with TiO₂ yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/pe-based-white-masterbatch-with-titanium-dioxide-tio%e2%82%82/feed/ 0 PE-Based Black Masterbatch https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/ https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/#respond Sun, 02 Nov 2025 10:41:05 +0000 https://hasacom.com/en/?post_type=product&p=1898 BCP-460 is a black polyethylene-based masterbatch containing 40% ultrafine ...

PE-Based Black Masterbatch yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> BCP-460 is engineered for general-purpose plastic applications, delivering high color uniformity, durability, and excellent dispersion.
Its formulation with antioxidants (AO), process aid (PPA), and functional fillers ensures consistent performance in both monolayer and multilayer extrusion systems.

Applications:

  • Pipes and conduit systems

  • Cable sheathing and insulation

  • Films and sheets

  • Household and automotive parts

Form: Black pellets
Process: Extrusion, Injection, Blow Molding

Key Features

  • 40% ultrafine carbon black content

  • Deep black tone and high opacity

  • Excellent dispersion and surface smoothness

  • UV and thermal stability

  • Wide processing temperature range

  • Suitable for LDPE, LLDPE, and HDPE systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 1.2 ± 0.1
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1 ± 0.5
Filler Content (Carbon Black) ISO 3451 % 40
Tensile Strength ISO 527 MPa 22
Elongation at Break ISO 527 % 700
Hardness ISO 868 Shore D 60
Vicat Softening Point ISO 306 °C 129
Oxidation Induction Time ISO 11357 min 30
Moisture Content ISO 15512 % < 0.25

Processing Guidelines

  • Barrel Temperature: 150–220 °C

  • Die Head Temperature: 220–230 °C

  • Compatible with standard PE screws

  • Excellent output and dispersion across multiple processing types

Packaging & Storage

Supplied in 25 kg bags or 850 kg big bags.
Store in original packaging under cool, dry conditions, away from sunlight and heat.
Recommended shelf life: 2 years.

PE-Based Black Masterbatch yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/polyethylene-based-black-masterbatch/feed/ 0 CaCO₃ Calcium Carbonate Filled PE Compound https://hasacom.com/en/urun/caco%e2%82%83-calcium-carbonate-filled-polyethylene-compound/ https://hasacom.com/en/urun/caco%e2%82%83-calcium-carbonate-filled-polyethylene-compound/#respond Sun, 02 Nov 2025 10:26:51 +0000 https://hasacom.com/en/?post_type=product&p=1894 CFP-180 is a cost-optimized, calcium carbonate filled polyethylene compound containing 10–80% ...

CaCO₃ Calcium Carbonate Filled PE Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> CFP-180 is a CaCO₃-filled polyethylene masterbatch engineered to improve mechanical and surface performance of polyolefin products.
It provides higher rigidity, gloss, and print adhesion, making it ideal for film, sheet, molding, and cable applications.

Applications:

  • Packaging films and sheets

  • Containers and bottles

  • Household and industrial goods

  • Cable sheathing and insulation

Form: Natural / White Pellets
Processing: Extrusion, Injection, Blow Molding

Key Features

  • Cost-effective filler compound for PE systems

  • Enhanced stiffness and surface finish

  • Excellent printability and dimensional stability

  • Wide processing window

  • Compatible with LDPE, LLDPE, and HDPE

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 0.96–1.60
Melt Flow Rate (190 °C / 5 kg) ISO 1133 g/10 min 0.5–2
Filler Content ISO 3451 % 10–80
Tensile Strength ISO 527 MPa 15–20
Elongation at Break ISO 527 % 300–500
Hardness ISO 868 Shore D 55–65
Vicat Softening Point ISO 306 °C 126
Oxidation Induction Time ISO 11357 min 20
Moisture Content ISO 15512 % < 0.25

Processing Guidelines

  • Extruder Barrel Temp: 150–220 °C

  • Die Head Temp: 220–230 °C

  • Suitable for most PE extrusion and molding lines

  • Recommended for PE screws and high-output systems

Packaging & Storage

Supplied in 25 kg bags or 850 kg big bags.
Store in original packaging, in a cool, dry, and clean area, away from sunlight and heat.
Shelf life: up to 2 years.

CaCO₃ Calcium Carbonate Filled PE Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.