PE Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/pe_compounds/ Hasa International trade goods import and export Sun, 02 Nov 2025 12:14:49 +0000 en-US hourly 1 https://wordpress.org/?v=6.9 https://hasacom.com/en/wp-content/uploads/2023/01/cropped-favicon-1-32x32.png PE Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/pe_compounds/ 32 32 HDPE UV-Stabilized Jacketing Compound https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/ https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/#respond Sun, 02 Nov 2025 10:00:49 +0000 https://hasacom.com/en/?post_type=product&p=1891 JAC03-UV is a UV-stabilized high-density polyethylene (HDPE) compound designed for cable ...

HDPE UV-Stabilized Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC03-UV is a natural-colorable HDPE compound with UV stabilizers and antioxidants for enhanced long-term durability.
It offers superior resistance to UV radiation, oil and termite attack, and excellent surface quality during extrusion.
The compound meets ASTM D1248 Type III Class A Category 5 Grade J5, IEC 60502 ST7, IEC 60840 ST7, and IEC 60708 standards.

Key Features

  • Excellent UV resistance and outdoor stability

  • Termite and oil resistance (UL 1072 Type I & II)

  • Low water permeability

  • Excellent environmental stress crack resistance (ESCR > 5000 h)

  • High tensile strength and elongation

  • Smooth surface extrusion and easy processing

Technical Specifications

Property Typical Value Test Method
Density 0.943 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) 0.33 ± 0.05 g/10 min ASTM D1238
Tensile Strength ≥ 27 N/mm² ASTM D638 / IEC 60811-1-1
Elongation at Break ≥ 800 % ASTM D638
Elongation after Ageing (10 days @ 110 °C) ≥ 500 % ASTM D638
Oxidation Induction Time (200 °C) ≥ 30 min ASTM D3895
ESCR (50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 60 ± 2 Shore D ASTM D2240
Vicat Softening Point ≥ 115 °C ISO 306
Hot Pressure Test (110 °C) < 50 % IEC 60811-3-1
Water Absorption ≤ 0.01 % ASTM D570
Volume Resistivity ≥ 10¹⁵ Ω·cm IEC 60093
Dielectric Strength (2 mm) No breakdown @ 10 kV/mm IEC 60243

Processing Recommendations

Recommended extrusion temperature profile (°C):
Zone 1 – 160–180 | Zone 2 – 170–190 | Zone 3 – 180–200 | Zone 4 – 190–210 | Head – 210–230 | Die – 240–260

Provides a smooth extrusion surface; adjust profile according to extruder type.

Applications

  • Outer jacketing for power and telecommunication cables

  • Outdoor UV-resistant cable systems

  • Industrial, marine, and energy cables exposed to sunlight

Packaging & Safety

Supplied in 25 kg PP laminated bags (pellet form).
Store below 30 °C, away from sunlight and humidity.
Classified as non-hazardous material.

HDPE UV-Stabilized Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/hdpe-uv-stabilized-jacketing-compound/feed/ 0 Black LLDPE Jacketing Compound https://hasacom.com/en/urun/black-lldpe-jacketing-compound/ https://hasacom.com/en/urun/black-lldpe-jacketing-compound/#respond Sun, 02 Nov 2025 08:14:04 +0000 https://hasacom.com/en/?post_type=product&p=1888 JAC04 is a black linear low-density polyethylene (LLDPE) compound designed for ...

Black LLDPE Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC04 is a carbon black-filled (2.5%) LLDPE compound optimized for cable jacketing applications.
Its high melting temperature, excellent petroleum-jelly resistance, and low moisture permeability ensure long-term cable durability under demanding environments.
The compound provides a smooth extrusion surface, broad processing window, and superior mechanical flexibility.

Complies with: ASTM D1248 Type 2, Class C, Category 4, Grade J3,

E5 IEC 60502 ST7 | EN 50290-2-23

Key Features

  • Excellent weathering and UV resistance (2.5% carbon black)

  • Good petroleum-jelly and oil resistance

  • Low water permeability

  • Superior ESCR (Environmental Stress Crack Resistance > 5000 h)

  • High tensile and elongation properties

  • Wide extrusion temperature range (140–230 °C)

  • Non-hazardous material

Technical Specifications

Property Typical Value Test Method
Density 0.935 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) ≤ 1.0 g/10 min ASTM D1238
Tensile Strength ≥ 20 N/mm² ASTM D638
Elongation at Break ≥ 800 % ASTM D638
Elongation after Ageing (240 h / 110 °C) ≥ 300 % ASTM D638
ESCR (Condition A, 50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 56 ± 2 Shore D ASTM D2240
Brittleness Temperature < –70 °C ASTM D746
O.I.T. (200 °C) > 100 min ASTM D3895
Carbon Black Content 2.5 % ASTM D1603
Carbon Black Dispersion ≤ 2 ISO 18553
Volume Resistivity 10¹⁵ Ω·cm IEC 60093
Dielectric Strength (2 mm) ≥ 20 kV/mm IEC 60243
Dielectric Constant (1 MHz) ≤ 2.3 ASTM D150
Dissipation Factor (1 MHz) ≤ 0.005 ASTM D150

Processing Recommendations

Recommended extrusion temperature profile (°C): Zone 1 – 140–160 | Zone 2 – 150–170 | Zone 3 – 160–180 | Zone 4 – 170–190 | Head – 200–220 | Die – 210–230
Preheating/drying max 80 °C.

Applications

  • Outer jacketing for power and communication cables

  • Outdoor and underground cable systems requiring UV and jelly resistance

  • Industrial and telecommunication installations

Packaging & Storage

Supplied as pellets in 25 kg PP laminated bags.
Store below 30 °C, away from direct sunlight and moisture.
Classified as non-hazardous.

Black LLDPE Jacketing Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/black-lldpe-jacketing-compound/feed/ 0 Black HDPE Compound for Cable Jacketing https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/ https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/#respond Sun, 02 Nov 2025 08:02:54 +0000 https://hasacom.com/en/?post_type=product&p=1885 JAC05 is a black high-density polyethylene (HDPE) compound designed ...

Black HDPE Compound for Cable Jacketing yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> JAC05 is a specially formulated HDPE compound used for the sheathing and insulation of power and communication cables.
The compound ensures outstanding weathering resistance, UV stability, termite protection, and mechanical strength under outdoor exposure.
Complies with ASTM D1248 Type III, Class C, Cat.5, Grade J5, IEC 60502 ST7, IEC 60840 ST7, IEC 60708 standards.

Key Features

  • Excellent UV resistance (2.5% carbon black)

  • Termite and oil resistance (UL 1072 Type I & II)

  • Superior ESCR (Environmental Stress Crack Resistance > 5000 h)

  • Low water permeability and weather stability

  • High mechanical strength and flexibility

  • Excellent surface finish during extrusion

Technical Specifications

Property Typical Value Test Method
Density 0.945 ± 0.005 g/cm³ ASTM D792
Melt Flow Index (190 °C / 2.16 kg) 0.29 ± 0.03 g/10 min ASTM D1238
Carbon Black Content 2.5 % ASTM D1603
Tensile Strength ≥ 25 N/mm² ASTM D638 / IEC 60811-1-1
Elongation at Break ≥ 700 % ASTM D638 / IEC 60811-1-1
Elongation after Ageing (14 days / 110 °C) ≥ 500 % ASTM D638
O.I.T. (Oxidation Induction Time @ 200 °C) ≥ 30 min ASTM D3895
ESCR (Condition B, 50 °C, 10% Igepal) > 5000 h ASTM D1693
Hardness 57 ± 1 Shore D ASTM D2240
Oil Immersion (70 °C, 4 h) Δ Tensile / Δ Elong. < 20 % / < 40 % ASTM D2633
Carbon Black Dispersion ≤ 2.5 ISO 18553
Hot Pressure Test (110 °C) < 50 % IEC 60811-3-1
Volume Resistivity ≥ 10¹⁶ Ω·cm IEC 60093
Dielectric Strength (2 mm) No breakdown @ 10 kV/mm IEC 60243

Processing Guidelines

Recommended Extrusion Temperatures (°C):

Zone 1 – 140–160 | Zone 2 – 150–170 | Zone 3 – 160–180 | Zone 4 – 170–190 | Head – 200–210 | Die – 210–220

Provides excellent surface quality; adjust temperatures according to extruder design.

Applications

  • Outer jacketing and insulation of power & communication cables

  • Outdoor cable systems requiring UV & oil resistance

  • Underground and termite-prone environments

Packaging & Safety

Supplied in 25 kg PP laminated bags (pellet form).
Store below 30 °C, away from sunlight and moisture.
Classified as non-hazardous material.

Black HDPE Compound for Cable Jacketing yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/black-hdpe-high-density-polyethylene-compound/feed/ 0