XLPE Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/xlpe_compounds/ Hasa International trade goods import and export Thu, 06 Nov 2025 12:15:16 +0000 en-US hourly 1 https://wordpress.org/?v=6.9 https://hasacom.com/en/wp-content/uploads/2023/01/cropped-favicon-1-32x32.png XLPE Compounds Archives - Hasacom https://hasacom.com/en/urun-kategori/polymer_compounds/xlpe_compounds/ 32 32 XLPE Compound for Low / Medium Voltage Cable Insulation https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/ https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/#respond Sun, 02 Nov 2025 11:27:12 +0000 https://hasacom.com/en/?post_type=product&p=1906 XBC-955 is a high-performance cross-linkable polyethylene (XLPE) compound engineered for low ...

XLPE Compound for Low / Medium Voltage Cable Insulation yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> XBC-955 is designed for the insulation of low & medium voltage (LV/MV) cables, offering superior thermal stability, dielectric strength, and mechanical integrity after curing.
It is suitable for moisture-cure, silane, or catalyst-based cross-linking systems and provides a smooth extrusion surface and consistent output on standard PE extrusion lines.

Applications:

  • Low and Medium Voltage Cable Insulation

  • Electrical Power Cables and Conductors

  • Building and Industrial Wire Insulation

Form: Natural Pellets
Process: Extrusion (Moisture / Silane Cross-Linking)

Key Features

  • Excellent mechanical properties after cross-linking

  • High tensile strength and elongation

  • Superior electrical insulation and volume resistivity

  • Good surface finish and extrusion stability

  • Compatible with moisture and silane cross-linking systems

Technical Specifications

Property Test Method Unit Typical Value
Density ISO 1183 g/cm³ 0.935 ± 0.005
Melt Flow Rate (190 °C / 2.16 kg) ISO 1133 g/10 min 1.5 ± 0.5
Tensile Strength ISO 527 MPa 22
Elongation at Break ISO 527 % 700
Hardness ISO 868 Shore D 58
Melting Point ISO 11357 °C 127
Oxidation Induction Time (200 °C) ISO 11357 min 60
ESCR (50 °C, F50) ISO 22088 h > 1000
Gel Content (After Cross-Linking) ISO 10147 % ≥ 65

Processing Recommendations

  • Barrel Temperature: 150 – 230 °C

  • Die Head Temperature: 230 – 240 °C

  • Suitable for PE screw extruders

  • Ensure moisture-free feeding and proper degassing for optimal cross-linking

Packaging & Storage

Supplied in 25 kg sacks.
Store in a cool, dry, clean area, away from sunlight and heat.
Recommended storage period: max 2 years.

XLPE Compound for Low / Medium Voltage Cable Insulation yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/xlpe-compound-for-low-medium-voltage-cable-insulation/feed/ 0 XLPE Compound Natural https://hasacom.com/en/urun/silane-cross-linkable-polyethylene-compound-xlp13-cat13n-natural-xlpe/ https://hasacom.com/en/urun/silane-cross-linkable-polyethylene-compound-xlp13-cat13n-natural-xlpe/#respond Sat, 01 Nov 2025 11:08:07 +0000 https://hasacom.com/en/?post_type=product&p=1848 XLP13 is a silane cross-linkable polyethylene compound designed for low-voltage (≤1 ...

XLPE Compound Natural yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> XLP13 is a pre-grafted polyethylene compound intended for moisture-cure crosslinking in cable insulation.
When mixed with 5 % of its catalyst masterbatch CAT13N, it forms a high-quality XLPE insulation layer with excellent thermal and electrical properties.
This compound is ideal for low-voltage power and control cables (up to 1 kV) and is compatible with high-speed extrusion lines.

Key Features
Natural XLPE compound for LV cable insulation
Excellent electrical resistivity and mechanical strength
Smooth surface finish and stable extrusion behavior
Long-term ageing resistance at 135 °C
Complies with BS 7870-5, IEC 60502-1

Technical Specifications

Property Typical Value Standard
Melt Flow Index (190 °C / 5 kg) 3.5 ± 0.5 g/10 min ASTM D1238
Density 0.92 ± 0.005 g/cm³ ASTM D792
Tensile Strength ≥ 20 N/mm² IEC 60811-1-1
Elongation at Break ≥ 500 % IEC 60811-1-1
Ageing (7 days @ 135 °C) Δ Tensile / Δ Elongation ≤ 25 % / ≤ 25 % IEC 60811-1-2
Hot-Set Test (200 °C, 0.2 MPa) Elong. ≤ 100 %, Perm. ≤ 10 % IEC 60811-2-1
Volume Resistivity (23 °C) ≥ 10¹⁶ Ω·cm ASTM D257
Water Absorption (85 °C) ≤ 1 mg/cm³ IEC 60502-2
Shrinkage (130 °C, 1 hr) ≤ 4 % IEC 60502-2

Processing Guidelines
Mix XLP13 + CAT13N in a 95:5 ratio at room temperature just before extrusion.
Extrusion zones: 140 – 190 °C (typical).

Crosslinking methods
Hot water 90 °C × 2–6 h
Steam 6–15 h

Applications
Insulation of low-voltage power and control cables
Suitable for XLPE insulation lines and continuous extrusion

Packaging & Storage
Supplied as pellets in 25 kg aluminum multilayer bags.
Store below 35 °C in dry conditions; use within 6 months and within 4 hours after opening.

XLPE Compound Natural yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/silane-cross-linkable-polyethylene-compound-xlp13-cat13n-natural-xlpe/feed/ 0 XLPE Carbon Black Filled Compound https://hasacom.com/en/urun/xlp12bc-cat12n-xlpe-silane-cross-linkable-polyethylene-compound/ https://hasacom.com/en/urun/xlp12bc-cat12n-xlpe-silane-cross-linkable-polyethylene-compound/#respond Sat, 01 Nov 2025 10:41:47 +0000 https://hasacom.com/en/?post_type=product&p=1843 XLP12BC is a silane cross-linkable polyethylene compound used for insulation of ...

XLPE Carbon Black Filled Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> XLP12BC is a pre-grafted polyethylene compound designed for moisture-cure crosslinking in cable insulation applications.
It is processed with its corresponding catalyst masterbatch CAT12N (5%) in standard extrusion lines.
The compound contains 2.5% carbon black for UV stability and weathering resistance, making it ideal for Aerial Bundled Cable (ABC) insulation.

Key Features & Advantages
Excellent weather and UV resistance (2.5% carbon black content)
Superior tensile strength and elongation
Reliable crosslinking through moisture exposure
Consistent extrusion performance and smooth surface finish
Complies with NF C 33-209, BS 7870-5, and IEC 60502-1

Technical Specifications

Property Typical Value Standard / Method
Melt Flow Index (190°C/5kg) 4 ± 0.5 g/10 min ASTM D1238
Density 0.930 ± 0.005 g/cm³ ASTM D792
Tensile Strength ≥ 18 N/mm² IEC 60811-1-1
Elongation at Break ≥ 400 % IEC 60811-1-1
Aging (10 days at 150°C) ΔTensile ≤ 25%, ΔElong. ≤ 25% IEC 60811-1-2
Hot Set Test (200°C, 0.3 MPa) Elongation ≤ 100%, Permanent ≤ 15% IEC 60811-2-1
Carbon Black Content 2.5 ± 0.5 % ASTM D1603

Processing Guidelines
Mix XLP12BC with CAT12N (95:5 ratio) at room temperature before extrusion.
Extrusion temperatures: 140–190°C (zone dependent).
Do not preheat or store premix for long durations.
Crosslinking by immersion in 90°C water (2–6 hrs) or steam (6–15 hrs).

Applications
Insulation of Aerial Bundled Cables (ABC)
Low and medium voltage insulation layers
Moisture-cured XLPE systems

Packaging & Storage
Supplied as pellets in 25 kg aluminum multilayer bags.
Store below 35°C, away from sunlight and humidity.
Use within 6 months of production and within 3–4 hours after opening.

XLPE Carbon Black Filled Compound yazısı ilk önce Hasacom üzerinde ortaya çıktı.

]]> https://hasacom.com/en/urun/xlp12bc-cat12n-xlpe-silane-cross-linkable-polyethylene-compound/feed/ 0